Table 3 Maj or element compositions of minerals and melts

From: Trace element partitioning between pyrochlore, microlite, fersmite and silicate melts

n 5   8   10   10      
  SE_Pyro2   SE_Pyro2   SE_Pyro3   SE_Pyro3      
  Fer   Melt   Nb-Pyr   Melt      
  av Stdev av Stdev av Stdev av Stdev     
Na2O n.d   0.4 0.04    0.24 0.08     
Al2O3 n.d   5.4 0.5    5.2 0.1     
CaO 17.4 0.5 31.3 0.8 28.6 0.4 31.3 0.8     
SiO2 n.d   28.2 0.2    28.2 0.2     
Ta2O5 n.a   n.a   n.a   n.a      
Nb2O5 80.8 0.03 30.7 0.1 68.4 0.2 30.7 0.1     
F 0.9 0.2 3.5 0.5 2.6 0.4 2.6 0.2     
Total 99.1   99.50   99.60   98.2      
n 3   10   2   8   10    
  SE_Pyro5   SE_Pyro5   SE_Pyro6   SE_Pyro6   SE_Pyro6    
  Fer   Melt   Fer   Nb-Pyr   Melt    
  av Stdev av Stdev av Stdev av Stdev av Stdev   
Na2O n.d   n.d   n.d   n.d   n.d    
Al2O3 n.d   6.1 0.9 n.d   n.d   6.3 0.1   
CaO 17.1 0.3 32.5 0.5 17.3 0.5 29.0   32.7 0.2   
SiO2 n.d   32.3 0.4 n.d   n.d   33.7 0.3   
Ta2O5 n.a   n.a   n.a   n.a   n.a    
Nb2O5 82.8 0.4 23.1 0.7 80.8 0.5 67.7   21.8 0.4   
F 0.5 0.2 4.2 0.6 0.8 0.3 2.4   3.1 0.3   
Total 100.4   98.2   98.9   99.2   97.6    
n 10   10   10   10   10   10  
  HW1     HW2     HW3    
  Ta-pyr   Melt   Ta-pyr   Melt   Ta-pyr   Melt  
  av Stdev av Stdev av Stdev av Stdev av Stdev av Stdev
Na2O 0.06 0.03 0.4 0.1 0.05 0.03 0.52 0.03 0.12 0.03 4.2 0.1
Al2O3 0.04 0.01 6.5 0.1 0.04 0.02 5.78 0.11 0.03 0.02 14.7 0.1
CaO 20.1 0.2 37.2 0.5 20.1 0.1 35.2 0.3 19.9 0.2 25.0 0.4
SiO2 0.04 0.03 41.1 0.7 0.05 0.04 37.2 0.2 0.04 0.03 45.0 0.4
Ta2O5 79.3 0.5 15.5 1.0 79.2 0.6 21.7 0.2 79.9 0.8 10.1 0.8
Nb2O5 0.13 0.05 0.09 0.04 0.13 0.04 0.1 0.1 0.10 0.05 0.02 0.01
Total 99.6 0.5 100.7 2.4 99.6 0.9 100.4 0.9 100.0 1.1 99.0 1.8
  1. Major element composition of minerals and quenched melts (Fer = Ca-Nb-fersmite, Nb-pyr = Ca-Nb-pyrochlore, melt = quenched melt, Ta—pyr = Ca-Ta-microlite) analyzed with EMPA. n number of analyses, n.d. not detected, n.a. not analyzed. Note that fersmite occurred in all runs with the SE_Pyro1 starting materials (Table 1) but in most runs these crystals were too small too be analyzed, and we only present data from runs SE_Pyro5 and SE_Pyro6.