Table 4 Trace element compositions of minerals and melts, and calculated partition coefficients

From: Trace element partitioning between pyrochlore, microlite, fersmite and silicate melts

  HW1          
n 7   6        
  Ta-Pyr Stdev Melt Stdev D Ta-pyr HW1 Stdev     
Li 1.0 0.1 12.7 0.3 0.08 0.01     
Sc 205 22 1100 14 0.19 0.02     
Mn 101 11 290 1 0.35 0.04     
Co 205 37 1290 10 0.16 0.03     
Ni 76 16 641 4 0.12 0.03     
Ga 21 11 791 13 0.03 0.01     
Ge 77 10 250 4 0.31 0.04     
Sr 187 3 477 3 0.39 0.01     
Y 708 105 707 4 1.0 0.1     
Zr 896 130 906 8 1.0 0.1     
Nb 999 92 777 12 1.3 0.1     
Mo 0.20 0.18 12.8 0.2 0.02 0.01     
Ba 33 9 736 7 0.04 0.01     
La 1111 173 448 6 2.5 0.4     
Ce 1070 361 191 3 5.6 1.9     
Nd 1695 389 490 8 3.5 0.8     
Sm 1408 323 466 4 3.0 0.7     
Gd 675 127 317 3 2.1 0.4     
Dy 565 91 372 2 1.5 0.2     
Yb 324 37 487 3 0.7 0.1     
Lu 558 64 1048 11 0.5 0.1     
Hf 1390 299 782 14 1.8 0.4     
Ta 590,712 27,309 121,645 5874 4.9 0.3     
Th 0.5 0.2 0.06 0.01 7.8 3.1     
U 1.6 0.3 4.0 0.1 0.4 0.1     
  HW2          
n 8   6        
  Ta-Pyr Stdev Melt Stdev D Ta-pyr HW2 Stdev     
Li 1.4 0.2 14.3 0.4 0.10 0.02     
Sc 187 25 985 10 0.19 0.03     
Mn 105 4 282 7 0.37 0.02     
Co 208 18 1197 12 0.17 0.01     
Ni 77 11 581 6 0.13 0.02     
Ga 18 5 705 9 0.03 0.01     
Ge 70 8 60 2 1.18 0.13     
Sr 180 3 448 5 0.40 0.01     
Y 678 73 674 16 1.01 0.11     
Zr 834 116 933 16 0.89 0.13     
Nb 899 45 882 10 1.02 0.05     
Mo 0.09 0.04 6.2 0.2 0.015 0.007     
Ba 30 4 660 7 0.05 0.01     
La 1067 74 481 5 2.2 0.2     
Ce 1053 203 240 4 4.4 0.9     
Nd 1693 212 543 7 3.1 0.4     
Sm 1388 178 503 8 2.8 0.4     
Gd 662 74 329 5 2.0 0.2     
Dy 550 57 371 6 1.5 0.2     
Yb 318 30 450 7 0.7 0.1     
Lu 545 45 964 15 0.57 0.05     
Hf 1326 202 848 18 1.6 0.2     
Ta 603,553 6796 167,305 2991 3.6 0.1     
Th 0.5 0.1 0.080 0.004 5.9 1.5     
U 0.9 0.1 3.56 0.03 0.26 0.02     
  HW3          
n 6   5        
  Ta-Pyr Stdev Melt Stdev D Ta-pyr HW3 Stdev     
Li 3.2 0.6 68 21 0.05 0.02     
Sc 112.8 48.9 1053 333 0.11 0.06     
Mn 66.5 19.5 517 152 0.13 0.05     
Co 109.5 43.9 3013 988 0.04 0.02     
Ni 33.4 18.1 1409 456 0.024 0.015     
Ga 10.5 1.2 1915 608 0.005 0.002     
Ge 85.3 8.3 1340 419 0.06 0.02     
Sr 196.5 6.5 904 291 0.22 0.07     
Y 717.7 41.7 235 69 3.1 0.9     
Zr 665.9 127.1 208 59 3.2 1.1     
Nb 831.0 13.7 487 148 1.7 0.5     
Mo 1.2 0.1 70 23 0.017 0.006     
Ba 34.1 2.2 1843 570 0.018 0.006     
La 1417 231 509 154 2.8 1.0     
Ce 1527 269 87 24 17.6 5.8     
Nd 2235 305 332 93 6.7 2.1     
Sm 1770 171 251 71 7.1 2.1     
Gd 778 35 138 39 5.6 1.6     
Dy 608 18 138 40 4.4 1.3     
Yb 304 31 148 43 2.0 0.6     
Lu 493 66 319 94 1.5 0.5     
Hf 1054 300 367 104 2.9 1.2     
Ta 589,199 9317 87,900 24,870 6.7 1.9     
Th 0.8 0.2 0.10 0.03 7.8 3.0     
U 1.5 0.3 12 4 0.12 0.04     
  SE_Pyro3          
n 5   5        
  Nb-pyr Stdev Melt stdev D Nb-pyr/melt SE3 Stdev     
Li 3.5 0.3 13 1 0.27 0.03     
Sc 315 151 1815 45 0.17 0.08     
Mn 102 34 482 4 0.21 0.07     
Co 298 157 1852 96 0.16 0.09     
Ni 158 90 977 47 0.16 0.09     
Ga 196 104 1125 64 0.17 0.09     
Ge 40 3 50 28 0.8 0.5     
Sr 547 10 618 12 0.88 0.02     
Y 893 53 1400 60 0.64 0.05     
Zr 697 139 2050 74 0.34 0.07     
Nb 489,667 38,502 273,134 6537 1.8 0.1     
Mo 10 1 27 5 0.37 0.09     
Ba 265 68 944 18 0.28 0.07     
La 1895 259 911 74 2 0.3     
Ce 994 70 670 34 1.5 0.1     
Nd 2376 314 1223 82 1.9 0.3     
Sm 1791 169 1098 56 1.6 0.2     
Gd 843 55 678 34 1.2 0.1     
Dy 665 18 737 34 0.9 0.05     
Yb 396 51 820 30 0.48 0.06     
Lu 762 133 1847 81 0.41 0.07     
Hf 901 105 1980 116 0.45 0.06     
Ta 4361 947 1142 100 3.8 0.9     
Th 167 6 196 11 0.85 0.06     
U 23 12 108 31 0.2 0.1     
  SE_Pyro4          
n 5   5        
  Nb-pyr Stdev melt Stdev D Nb-pyr/melt SE4 Stdev     
Li 5.3 0.4 11.7 0.5 0.97 0.09     
Sc 551 182 1822 18 0.82 0.27     
Mn 127 59 514 3 0.7 0.3     
Co 363 270 2034 52 0.58 0.43     
Ni 188 125 1032 25 0.6 0.4     
Ga 196 147 1008 23 0.5 0.4     
Ge 123 67 288 191 2.3 2.0     
Sr 568 18 606 18 1.31 0.06     
Y 825 168 1421 24 1.10 0.20     
Zr 1180 190 2058 47 1.20 0.20     
Nb 481,096 60,016 268,189 9708 1.50 0.20     
Mo 8.5 0.8 18 4 0.8 0.2     
Ba 339 108 962 20 0.9 0.3     
La 1916 147 841 21 1.6 0.1     
Ce 932 59 643 10 1.43 0.09     
Nd 2359 141 1176 28 1.6 0.1     
Sm 1681 94 1065 21 1.47 0.09     
Gd 784 73 668 13 1.40 0.10     
Dy 609 91 739 15 1.20 0.20     
Yb 379 118 835 14 0.90 0.30     
Lu 753 279 1919 64 0.90 0.30     
Hf 1561 247 1997 70 1.4 0.2     
Ta 3862 1055 1084 85 1.6 0.5     
Th 199 22 189 4 1.41 0.2     
U 38 25 133 44 0.91 0.7     
  SE_Pyro5          
n 5   5        
  Fer Stdev melt Stdev D fer/melt SE5 Stdev     
Li 4.2 1.0 13.6 0.5 0.31 0.07     
Sc 388 214 2292 14 0.17 0.09     
Mn 94 57 602 5 0.16 0.09     
Co 328 253 2281 24 0.1 0.08     
Ni 160 84 1144 14 0.14 0.07     
Ga 187 145 1194 12 0.2 0.1     
Ge 13 2 51 9 0.24 0.06     
Sr 175 76 736 16 0.20 0.10     
Y 918 166 1609 40 0.60 0.10     
Zr 1269 248 2462 81 0.50 0.10     
Nb 474,314 123,606 253,661 11,699 1.9 0.5     
Mo 13 3 20 0 0.6 0.1     
Ba 178 138 1187 39 0.1 0.08     
La 483 74 973 35 0.5 0.08     
Ce 349 44 719 19 0.49 0.06     
Nd 1034 185 1262 34 0.8 0.1     
Sm 973 207 1145 27 0.8 0.2     
Gd 611 137 725 19 0.8 0.2     
Dy 582 133 818 28 0.7 0.2     
Yb 454 75 950 31 0.48 0.08     
Lu 967 137 2200 74 0.44 0.06     
Hf 1334 288 2501 91 0.5 0.1     
Ta 2973 749 812 33 3.7 0.9     
Th 95 20 227 7 0.42 0.09     
U 9 3 163 12 0.05 0.02     
  SE_Pyro6          
n 5   2   5      
  Nb-pyr Stdev Fer Stdev Melt Stdev D Nb-pyr/melt SE6   D fer/melt SE6  
Li 3 10.3 0.2 0.25
Sc 62 9 70 51 2240 11 0.028 0.004 0.03 0.02
Mn 33 9 26 2 570 5 0.06 0.02 0.045 0.0003
Co 43 22 14 3 2191 24 0.02 0.01 0.006 0.001
Ni 13 5 1115 14 0.012 0.004
Ga 6.6 1.1 1.2 0.5 1286 19 0.0051 0.0009 0.001 0.0004
Ge 22 2 13 4 23.6 1.0 0.92 0.08 0.5 0.2
Sr 366 7 92 3 781 15 0.47 0.01 0.117 0.005
Y 555 20 1001 314 1539 30 0.36 0.02 0.7 0.2
Zr 319 39 1372 439 2300 45 0.14 0.02 0.6 0.2
Nb 398,834 6729 803,171 23,398 209,001 6675 1.91 0.07 3.8 0.2
Mo 5.7 0.5 11.9 0.6 47.8 1.0 0.12 0.01 0.25 0.01
Ba 98 4 1.7 0.5 1167 29 0.084 0.004 0.0015 0.0005
La 1439 109 343 143 1265 27 1.14 0.09 0.3 0.1
Ce 712 31 282 126 858 21 0.83 0.04 0.3 0.1
Nd 1824 125 1089 361 1504 32 1.21 0.09 0.7 0.2
Sm 1291 75 1119 353 1266 30 1.02 0.06 0.9 0.3
Gd 597 25 742 214 738 16 0.81 0.04 1.0 0.3
Dy 434 12 682 207 796 20 0.55 0.02 0.9 0.3
Yb 208 8 448 170 908 22 0.23 0.01 0.5 0.2
Lu 380 19 896 333 2128 47 0.18 0.01 0.4 0.2
Hf 484 63 1180 579 2343 53 0.21 0.03 0.5 0.2
Ta 4050 593 4490 497 985 18 4.1 0.6 4.6 0.5
Th 108 16 64 54 241 5 0.45 0.07 0.3 0.2
U 2.9 0.8 11 6 81 4 0.04 0.01 0.13 0.08
  SE_Pyro2          
n 2   5        
  Fer Stdev melt Stdev D fer/melt SE2      
Li 11.2 0.2     
Sc 3.0 0.04 -     
Mn 2.5 22.7 0.5 0.11     
Co 1.3 0.4 32.6 0.4 0.04     
Ni 85.6 3.3     
Ga 4.4 0.2     
Ge 2.6 17.6 0.3 0.15     
Sr 15.6 1.9 123 1 0.13     
Y 5.5 0.44 4.1 0.1 1.3 0.2     
Zr 31 12 80 1 0.38 0.03     
Nb 583,356 17,353 253,850 3380 2.3 0.9     
Mo 10.4 0.9 52.3 0.9 0.2 0.007     
Ba 0.7 0.2 13.5 0.4 0.05 0.01     
La 1.6 0.2 2.55 0.04 0.6 0.1     
Ce 2.5 0.3 3.8 0.1 0.67 0.08     
Nd 3.4 0.4 2.5 0.1 1.3 0.2     
Sm 8.8 0.9 5.5 0.1 1.6 0.2     
Gd 3.1 0.4 1.8 0.1 1.7 0.2     
Dy 2.5 0.3 1.7 0.1 1.5 0.2     
Yb 1.8 0.1 1.9 0.1 1.0 0.1     
Lu 1.7 0.2 1.9 0.1 0.86 0.06     
Hf 1.2 0.6 3.0 0.1 0.41 0.04     
Ta 39.6 0.8 13.5 0.1 2.9 1.3     
Th 0.8 0.1 1.14 0.04 0.7 0.1     
U 0.28 0.04 3.08 0.03 0.09 0.01     
  1. Fer = Ca-Nb-fersmite, Nb-pyr = Ca-Nb-pyrochlore, melt = quenched melt, Ta—pyr = Ca- Ta-microlite, stdev = standard deviation (2 sigma)